隨著各種焊接設備的增加與運用，自動化行業(yè)也在快速發(fā)展，其中不銹鋼焊機焊接設備也是許多商家會選擇的一種，那你知道不銹鋼自動焊接焊機設備有哪些注意事項嗎？下面山東焊接專機廠家為您講解：

With the increase and application of various welding equipment, the automation industry is also developing rapidly. Among them, stainless steel welding equipment is also a type that many businesses will choose. Do you know what precautions should be taken for stainless steel automatic welding equipment? Below, Shandong welding machine manufacturer will explain to you:

不銹鋼自動焊機焊接使用的范圍多是特殊的焊接材料，在使用范圍上主要以鈑金焊接、不銹鋼薄板的焊接、模具儀器、精密電子、缺陷修復為主。不銹鋼自動焊機焊接設備主要注意事項如下：

The welding range of stainless steel automatic welding machines is mostly special welding materials, mainly including sheet metal welding, stainless steel sheet metal welding, mold instruments, precision electronics, and defect repair. The main precautions for stainless steel automatic welding equipment are as follows:

1、使用橫向外特性的電源，直流時使用正極性（焊絲接負極）。

1. Use a power supply with lateral external characteristics, and use positive polarity (welding wire connected to negative electrode) for direct current.

2、一般適合6mm以下薄板的焊，具備焊縫成型美觀，焊變形量小的特點。

2. Generally suitable for welding thin plates below 6mm, with the characteristics of beautiful weld formation and small welding deformation.

3、維護氣體為氬氣，純度為99.99%。當焊電流為50--50A時，氬氣流量為8--0L/min，當電流為50--250A時，氬氣流量為2--5L/min。

3. The maintenance gas is argon with a purity of 99.99%. When the welding current is 50-50A, the argon flow rate is 8-0L/min, and when the current is 50-250A, the argon flow rate is 2-5L/min.

4、鎢極從氣體燃燒室引人注目的長度，以4--5mm為佳，，在角焊等遮擋性差的地方是2--3mm，在開槽深的地方是5--6mm，燃燒室工作的距離一般不多達5mm。

4. The striking length of the tungsten electrode from the gas combustion chamber is 4-5mm, which is preferred. In areas with poor shielding such as fillet welding, it is 2-3mm, and in areas with deep grooves, it is 5-6mm. The distance from the combustion chamber to the working area is generally not more than 5mm.

5、為避免焊氣孔之經常出現，焊部位如有鐵銹、油污等務必清掃整潔。

5. To avoid frequent occurrence of welding pores, any rust, oil stains, etc. on the welding area must be cleaned and cleaned.

6、焊電弧長度，焊普通鋼時，以2--4mm為佳，而焊不銹鋼時，以1--3mm為佳，過長則維護效果不好。

6. When welding ordinary steel, 2-4mm is the optimal arc length, while when welding stainless steel, 1-3mm is the optimal arc length. If it is too long, the maintenance effect is not good.

7、接入打底時，為避免底層焊道的背面被水解，背面也必須實體維護。

7. When connecting to the bottom layer, gas maintenance must also be carried out on the back side to avoid hydrolysis of the bottom layer weld bead.

8、為使氬氣不錯地維護焊熔池，和便于施焊操作者，鎢極中心線與焊處工件一般應維持80--85°角,填滿焊絲與工件表面夾角應盡可能地小，一般為0°左右。

8. In order to maintain the welding pool well with argon gas and facilitate welding operators, the center line of the tungsten electrode should generally maintain an angle of 80-85 ° with the workpiece at the welding point, and the angle between the filled welding wire and the surface of the workpiece should be as small as possible, usually around 0 °.

9、防風與換氣，有風的地方，務請采行擋網的措施，而在室內則應采行必要的換氣措施。

9. Wind prevention and ventilation. In windy areas, it is important to adopt measures such as mesh blocking, while indoors, necessary ventilation measures should be taken.

通過以上注意事項的介紹，相信您對不銹鋼自動焊機焊接設備有了一定的了解。如果有這方面的問題請點擊鏈接提交需求，我們http://www.oimhc.com幫你提供解決方案。

Through the introduction of the above precautions, I believe you have a certain understanding of stainless steel automatic welding equipment. If you have any questions in this regard, please click on the link to submit the requirements. We http://www.oimhc.com Help you provide a solution.